Normas AA Grau 5083 O
Propriedades
Em geral
| Propriedade | Valor | Condição | Padrões relacionados |
|---|---|---|---|
| Densidade | 2,66 g/cm³ | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Mecânico
| Propriedade | Valor | Condição | Padrões relacionados | Comentário |
|---|---|---|---|---|
| Módulo elástico | 71,0 GPa | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |
| Tenacidade à fratura por deformação plana | 22,0 - 35,0 MPa·√m | Típico para alumínio forjado da série 5000 | ||
| Razão de Poisson | 0,33 [-] | Típico para alumínio forjado da série 5000 | ||
| Módulo de cisalhamento | 26,0 - 26,5 GPa | Típico para alumínio forjado da série 5000 | ||
| Resistência à tracção | 250,0 MPa | O | Normas AA, ASTM B209 | |
| 255,0 MPa | O | Normas AA, ASTM B209 | ||
| 260,0 MPa | O | Normas AA, ASTM B209 | ||
| 270,0 - 345,0 MPa | O | Padrões AA, ASTM B209, ASTM B547 | ||
| 270,0 - 350,0 MPa | O | Padrões AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345 | ||
| 275,0 - 350,0 MPa | O | Padrões AA, ASTM B209, ASTM B547 | ||
| 290,0 MPa | O | Padrões AA |
Térmico
| Propriedade | Temperatura | Valor | Condição | Padrões relacionados | Comentário |
|---|---|---|---|---|---|
| Coeficiente de expansão térmica | 20°C | 2.38e-05 1/K | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |
| 100°C | 2.38e-05 1/K | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | ||
| Temperatura máxima de serviço | 150,0°C | Típico para alumínio forjado da série 5000 | |||
| Ponto de fusão | 580,0 - 640,0°C | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | ||
| Capacidade de calor específico | 879,0 - 963,0 J/(kg·K) | Típico para alumínio forjado da série 5000 | |||
| Condutividade térmica | 117,0 | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Elétrico
| Propriedade | Valor | Condição | Padrões relacionados |
|---|---|---|---|
| Condutividade elétrica | 17000000,0 S/m | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
| Resistividade elétrica | 5,88e-08 Ω·m | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Propriedades quimicas
| Propriedade | Valor | Condição | Padrões relacionados |
|---|---|---|---|
| Cromo | 0,05 - 0,25% | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
| Cobre | 0,1% | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
| Ferro | 0,40% | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
| Magnésio | 4,0 - 4,9% | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
| Manganês | 0,4 - 1,0% | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
| Silício | 0,4% | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
| Titânio | 0,15% | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
| Zinco | 0,25% | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Propriedades tecnológicas
| Propriedade | ||
|---|---|---|
| Brasagem | geral:nenhuma brasagem é conhecida ou desenvolvida | |
| Propriedades de corrosão | Fendas por corrosão sob tensão:como Schadensfall em Betrieb e bei Labortests (O, H321, H116), como Schadensfall em Betrieb, eingeschränkte Schäden bei den Labortests (H111), geral:muito bom, sem proteção em atmosfera industrial ou de água do mar | |
| Usinabilidade geral | Geral:pobre | |
| Trabalhabilidade | geral (condição):aceitável (O), ruim (H321, H116, H111) | |
Metal