AA 6061-O: Liga de Alumínio Versátil para Fabricação e Resistência à Corrosão
A liga AA 6061 é amplamente disponível e oferece excelente acabamento superficial, podendo ser anodizada com facilidade. Apresenta boa soldabilidade e brasabilidade, mantendo um acabamento superficial de qualidade. Possui resistência à corrosão em água do mar e condições atmosféricas, sendo também adequada para forjamento a quente.
Propriedades
Gerais
| Propriedade | Valor | Condição | Normas Relacionadas |
|---|---|---|---|
| Densidade | 2,7 g/cm³ | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Mecânicas
| Propriedade | Valor | Condição | Normas Relacionadas | Comentário |
|---|---|---|---|---|
| Resistência à fadiga de flexão | 60,0 MPa | O | Normas AA | |
| Módulo de elasticidade | 69,0 GPa | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
| Dureza Brinell | 30,0 | O | Normas AA | |
| Tenacidade à fratura em deformação plana | 22,0 - 35,0 MPa·√m | Típico para Alumínio Forjado Série 6000 | ||
| Coeficiente de Poisson | 0,33 | Típico para Alumínio Forjado Série 6000 | ||
| Módulo de cisalhamento | 26,0 - 26,5 GPa | Típico para Alumínio Forjado Série 6000 | ||
| Resistência à tração | 125,0 MPa | O | Normas AA | |
| Resistência à tração | 150,0 MPa | O | Normas AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B483 | |
| Resistência à tração | 155,0 MPa | O | Normas AA, ASTM B211, ASTM B316 |
Térmicas
| Propriedade | Temperatura | Valor | Condição | Normas Relacionadas | Comentário |
|---|---|---|---|---|---|
| Coeficiente de expansão térmica | 20 °C | 2,36e-05 1/K | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
| Coeficiente de expansão térmica | 100 °C | 2,36e-05 1/K | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
| Ponto de fusão | 580,0 - 650,0 °C | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | ||
| Calor específico | 887,0 - 963,0 J/(kg·K) | Típico para Alumínio Forjado Série 6000 | |||
| Condutividade térmica | 155,0 - 180,0 W/(m·K) | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Elétricas
| Propriedade | Valor | Condição | Normas Relacionadas |
|---|---|---|---|
| Condutividade elétrica | 23.000.000 - 27.000.000 S/m | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Resistividade elétrica | 3,7e-08 - 4,35e-08 Ω·m | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Composição Química
| Elemento | Teor (%) | Condição | Normas Relacionadas |
|---|---|---|---|
| Cromo | 0,04 - 0,35 | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Cobre | 0,15 - 0,40 | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Ferro | 0,70 | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Magnésio | 0,8 - 1,2 | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Manganês | 0,15 | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Silício | 0,4 - 0,8 | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Titânio | 0,15 | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Zinco | 0,25 | O | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Propriedades Tecnológicas
| Propriedade | Avaliação |
|---|---|
| Brasagem | Possível com processos e métodos comerciais |
| Propriedades de corrosão | Trinca por corrosão sob tensão: sem danos em operação e testes laboratoriais (O, T6, T651, T652, T6510, T6511); sem danos em operação, danos limitados em testes laboratoriais (T4, T451, T4510, T4511); geral: boa, sem proteção em atmosfera industrial ou marítima |
| Maquinabilidade geral | Geral: ruim (O), suficiente (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511) |
| Trabalhabilidade | Geral (condição): boa (O), aceitável (T4, T451, T4510, T4511), ruim (T6, T651, T652, T6510, T6511) |
Liga AW-6056 T78 – AlMgSi de Alta Resistência Endurecível por Envelhecimento (EN 573-3)
AW-6060 T64: Liga de Alumínio de Alto Desempenho e Segura para Alimentos (Grau EN 573-3)
Metal
- Liga de Alumínio AA 6061 H13 – Alta Resistência, Resistente à Corrosão e Facilmente Soldada
- Liga de Alumínio AA 5456 O – Propriedades Mecânicas Principais (Condição Recozida)
- Liga de Alumínio AA 5083-O: Alta Resistência e Resistência à Corrosão
- Liga de Alumínio AA 6066 T6 – Especificações Completas segundo Normas AA/ASTM
- Liga AA 6351 T6 – Propriedades Técnicas e Normas do Alumínio
- Liga AA 6061 T89 – Grau Premium, Resistente à Corrosão e Fácil Fabricação
- Liga de Alumínio AA 6061 T94 – Grau de Alto Desempenho 6061 com Acabamento T94
- Liga de Alumínio Grau 5454 O (Normas AA) – Especificação Completa
- Liga de Alumínio AA 1060 O – Especificações Completas e Normas
- Liga AA 3004 O: Propriedades Completas e Visão Geral de Desempenho