Liga AA 6061 T4 – Alumínio de Alto Desempenho para Soldagem, Brasagem e Anodização
A liga AA 6061 é uma das ligas de alumínio mais versáteis e amplamente disponíveis, reconhecida pelo excelente acabamento superficial e capacidade de anodização. Apresenta boa soldabilidade e brasabilidade, mantendo um acabamento de qualidade. Oferece resistência à corrosão em água do mar e condições atmosféricas, sendo também adequada para forjamento a quente.
Propriedades
Gerais
| Propriedade | Valor | Condição | Normas Relacionadas |
|---|---|---|---|
| Densidade | 2,7 g/cm³ | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
Mecânicas
| Propriedade | Valor | Condição | Normas Relacionadas | Comentário |
|---|---|---|---|---|
| Resistência à fadiga em flexão | 95,0 MPa | T4 | Normas AA | |
| Módulo de elasticidade | 69,0 GPa | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | |
| Dureza Brinell | 65,0 HB | T4 | Normas AA | |
| Tenacidade à fratura em deformação planar | 22,0 – 35,0 MPa·√m | – | – | Típico para alumínio forjado série 6000 |
| Coeficiente de Poisson | 0,33 | – | – | Típico para alumínio forjado série 6000 |
| Módulo de cisalhamento | 26,0 – 26,5 GPa | – | – | Típico para alumínio forjado série 6000 |
| Resistência à tração | 180,0 MPa | T4 | Normas AA, ASTM B221, ASTM B241, ASTM B345 | |
| Resistência à tração | 205,0 MPa | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | |
| Resistência à tração | 240,0 MPa | T4 | Normas AA |
Térmicas
| Propriedade | Temperatura | Valor | Condição | Normas Relacionadas | Comentário |
|---|---|---|---|---|---|
| Coeficiente de expansão térmica | 20 °C | 2,36×10⁻⁵ 1/K | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | |
| Coeficiente de expansão térmica | 100 °C | 2,36×10⁻⁵ 1/K | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | |
| Ponto de fusão | – | 580,0 – 650,0 °C | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | |
| Calor específico | – | 887,0 – 963,0 J/(kg·K) | – | – | Típico para alumínio forjado série 6000 |
| Condutividade térmica | – | 155,0 – 180,0 W/(m·K) | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
Elétricas
| Propriedade | Valor | Condição | Normas Relacionadas |
|---|---|---|---|
| Condutividade elétrica | 23.000.000 – 27.000.000 S/m | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Resistividade elétrica | 3,7×10⁻⁸ – 4,35×10⁻⁸ Ω·m | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
Composição Química
| Elemento | Teor (%) | Condição | Normas Relacionadas |
|---|---|---|---|
| Cromo | 0,04 – 0,35 | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Cobre | 0,15 – 0,40 | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Ferro | 0,70 máx. | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Magnésio | 0,8 – 1,2 | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Manganês | 0,15 máx. | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Silício | 0,4 – 0,8 | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Titânio | 0,15 máx. | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Zinco | 0,25 máx. | T4 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
Propriedades Tecnológicas
| Propriedade | Descrição |
|---|---|
| Brasagem | Possível com processos e métodos comerciais |
| Propriedades de corrosão | Trinca por corrosão sob tensão: sem danos em operação e testes de laboratório (O, T6, T651, T652, T6510, T6511); sem danos em operação, danos limitados em testes de laboratório (T4, T451, T4510, T4511); geral: boa, sem proteção em atmosfera industrial ou marítima |
| Usinabilidade geral | Geral: ruim (O), suficiente (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511) |
| Trabalhabilidade | Geral (condição): boa (O), aceitável (T4, T451, T4510, T4511), ruim (T6, T651, T652, T6510, T6511) |
Liga EN AW-6063 T64 (EN 573-3) – Alumínio Arquitetônico com Acabamento Superior e Resistência à Corrosão
Liga AA 2024 T4 – Alumínio de Alta Resistência e Excelente Usinabilidade para Aeronáutica
Metal
- Liga de Alumínio AA 6061 H13 – Alta Resistência, Resistente à Corrosão e Facilmente Soldada
- Liga de Alumínio AA 5456 O – Propriedades Mecânicas Principais (Condição Recozida)
- Liga de Alumínio AA 5083-O: Alta Resistência e Resistência à Corrosão
- Liga de Alumínio AA 6066 T6 – Especificações Completas segundo Normas AA/ASTM
- Liga AA 6351 T6 – Propriedades Técnicas e Normas do Alumínio
- Liga AA 6061 T89 – Grau Premium, Resistente à Corrosão e Fácil Fabricação
- Liga de Alumínio AA 6061 T94 – Grau de Alto Desempenho 6061 com Acabamento T94
- Liga de Alumínio Grau 5454 O (Normas AA) – Especificação Completa
- Liga de Alumínio AA 1060 O – Especificações Completas e Normas
- Liga AA 3004 O: Propriedades Completas e Visão Geral de Desempenho