Liga de Alumínio AA 6061-T6 (T62): Alta Resistência e Resistência à Corrosão
A liga de alumínio AA 6061-T6 (T62) é amplamente disponível e oferece excelente acabamento superficial, sendo facilmente anodizada. Apresenta boa soldabilidade e brasagem, mantendo um acabamento de qualidade. Possui resistência à corrosão em ambientes marinhos e atmosféricos, sendo adequada para forjamento a quente.
Propriedades Gerais
| Propriedade | Valor | Condição | Normas Relacionadas |
|---|---|---|---|
| Densidade | 2,7 g/cm³ | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Propriedades Mecânicas
| Propriedade | Valor | Condição | Normas Relacionadas | Comentário |
|---|---|---|---|---|
| Módulo de elasticidade | 69,0 GPa | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
| Tenacidade à fratura em tensão plana | 22,0 - 35,0 MPa·√m | Típico para alumínio forjado série 6000 | ||
| Coeficiente de Poisson | 0,33 [-] | Típico para alumínio forjado série 6000 | ||
| Módulo de cisalhamento | 26,0 - 26,5 GPa | Típico para alumínio forjado série 6000 | ||
| Resistência à tração | 260,0 MPa | T62 | Normas AA, ASTM B221, ASTM B241, ASTM B345 | |
| Resistência à tração | 275,0 MPa | T62 | Normas AA, ASTM B209 | |
| Resistência à tração | 290,0 MPa | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B483 |
Propriedades Térmicas
| Propriedade | Temperatura | Valor | Condição | Normas Relacionadas | Comentário |
|---|---|---|---|---|---|
| Coeficiente de expansão térmica | 20 °C | 2,36e-05 1/K | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
| Coeficiente de expansão térmica | 100 °C | 2,36e-05 1/K | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
| Ponto de fusão | 580,0 - 650,0 °C | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | ||
| Calor específico | 887,0 - 963,0 J/(kg·K) | Típico para alumínio forjado série 6000 | |||
| Condutividade térmica | 155,0 - 180,0 W/(m·K) | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Propriedades Elétricas
| Propriedade | Valor | Condição | Normas Relacionadas |
|---|---|---|---|
| Condutividade elétrica | 23.000.000 - 27.000.000 S/m | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Resistividade elétrica | 3,7e-08 - 4,35e-08 Ω·m | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Composição Química
| Elemento | Teor (%) | Condição | Normas Relacionadas |
|---|---|---|---|
| Cromo | 0,04 - 0,35 | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Cobre | 0,15 - 0,40 | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Ferro | 0,70 | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Magnésio | 0,8 - 1,2 | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Manganês | 0,15 | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Silício | 0,4 - 0,8 | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Titânio | 0,15 | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Zinco | 0,25 | T62 | Normas AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Propriedades Tecnológicas
| Propriedade | Descrição |
|---|---|
| Brasagem | Geral: possível com processos e métodos comerciais |
| Propriedades de corrosão | Trinca por corrosão sob tensão: sem danos em operação e testes de laboratório (O, T6, T651, T652, T6510, T6511), sem danos em operação, danos limitados em testes de laboratório (T4, T451, T4510, T4511). Geral: boa, sem proteção em atmosfera industrial ou marítima. |
| Usinabilidade geral | Geral: ruim (O), suficiente (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511) |
| Trabalhabilidade | Geral (condição): boa (O), aceitável (T4, T451, T4510, T4511), ruim (T6, T651, T652, T6510, T6511) |
AW-6060 H18: Liga AlMgSi Endurecível por Envelhecimento, Apta para Alimentos, para Aplicações de Alto Desempenho
Liga AA 6061 T1: Liga Premium para Aplicações Resistentes à Corrosão e Soldáveis
Metal
- ASTM B210 6061-T6/T62 – Alumínio com Soldabilidade Superior, Resistência à Corrosão e Desempenho em Anodização
- Normas AA Liga 6463 T62: Principais Propriedades Mecânicas e Especificações
- Liga de Alumínio AA 6066-T6 – Grau T62: Normas e Propriedades Mecânicas
- Liga de Alumínio AA 6061 H13 – Alta Resistência, Resistente à Corrosão e Facilmente Soldada
- ASTM B483 Grau 6061 T6/T62 Liga de Alumínio – Alta Resistência & Resistência à Corrosão
- ASTM B211 Grau 6061 T6, T62 e T651: Alumínio de Alta Resistência, Resistência à Corrosão e Versatilidade
- Liga de Alumínio AA 5456 O – Propriedades Mecânicas Principais (Condição Recozida)
- Liga de Alumínio AA 5083-O: Alta Resistência e Resistência à Corrosão
- Liga de Alumínio AA 6066 T6 – Especificações Completas segundo Normas AA/ASTM
- Liga AA 6351 T6 – Propriedades Técnicas e Normas do Alumínio